Velocidad de corrosión por inmersión y cámara de niebla salina
View/ Open
Item Links
URI: http://hdl.handle.net/20.500.1 ...Share
View Statistics
View Usage StatisticsMetadata
Show full item recordDirector/Asesor
Director. Santos Jaimes, AlfonsoDate
2018Tipo de contenido
Trabajo de grado
Abstract
Con el avance de la humanidad y en paralelo con las exigencias que esto conlleva, cada dra se exige mas a la industria para que logre estar a la altura de dichos requerimientos. Es relevante el conocimiento que se tenga respecto a Ia corrosion, en especial los mecanismos que puedan mitigar dicho proceso permitiendo, ademas, disminuir las perdidas econ6micas generadas por esta. Para Ia ejecuci6n del proyecto se emple6 un estudio experimental en un acero comiin: SAE 1020, sabiendo que la corrosion influye directamente a este material, se aplicaron diversos recubrimientos tales como el carburo de tungsteno, la alOmina, y el di6xido de titanio. Estos, se adhirieron a las placas metalicas que estaban siendo material de investigaci6n por un proceso Ilamado rociado termico; lo anterior, con el fin de mejorar las propiedades ffsicas y mecanicas del acero. Como objeto principal del proyecto, se determin6 la velocidad de corrosion tanto en las laminas que contaron con los recubrimientos anteriormente ... The progress of the humankind entails new demands. Every day the industry sector requires new developments to achieve these demands. It is required every day more to the industry in order that it manages to be at a height of sayings, Especially the mechanisms that could mitigate the above-mentioned process allowing, also, to diminish the economic losses generated for is. For develop the project an experimental study was used in a common steel: SAE1020, knowing that the corrosion influences directly to this material, there were applied such diverse coverings as the carbide of tungsten, alumina, and dioxide of titanium. These, Adherer to the metallic plates that were a material of investigation for a so called dewy thermal process; the previous thing, to improve the physical and mechanical properties of the steel. As principal object of the project, the speed of corrosion decided so much in the sheets that possessed the coverings previously mentioned, as those to which they were not exposed ...
Keyword/s
Corrosión y anticorrosivos
Velocidad
Normas técnicas - ASTM G-31
Normas técnicas - ASTM b - 117
Cámara de niebla