Evaluación de la resistencia a la flexión en vigas de concreto simple con presencia de juntas frías verticales e inclinadas tratadas epoxicamente

dc.contributor.advisorDirector. López Morantes, Elkin Mauricio
dc.contributor.authorGualdrón Nieto, Juan David
dc.contributor.authorRey García, Jessica Alejandra
dc.coverage.temporal2020es_CO
dc.date.accessioned2021-11-25T16:57:52Z
dc.date.available2021-11-25T16:57:52Z
dc.date.issued2020-07
dc.identifier.urihttp://hdl.handle.net/20.500.11912/9691
dc.description141p.: (pdf); il; imágenes; gráficas; tablas; anexos.es_CO
dc.description.abstractComúnmente los elementos que están compuestos de concreto deben ser interrumpidos por diversos incidentes presentados en el momento de realizar el proceso de fundición, provocando una discontinuidad en el elemento y apareciendo una grieta de unión más conocida como junta fría, afectando la resistencia de este, por esto, es necesario crear un puente de adherencia entre los dos tipos de concreto que forman el elemento para evitar que se presente un mayor riesgo de falla. Por tal motivo, en esta investigación se logró evaluar y correlacionar la resistencia a la flexión en vigas de concreto simple con un (F’c) de 3000 Psi o 21 MPa parcialmente endurecido a diferentes edades 7, 14 y 28 días con presencia de juntas frías verticales (90°) e inclinadas (45°), cuyo tiempo de formación fue de 4, 6 y 8 horas, empleando como puente de adherencia el adhesivo SIKADUR® 32 Primer. Se elaboraron 108 especímenes distribuidos de la siguiente manera, 72 vigas con juntas frías verticales (90°) e inclinadas (45°) tratadas y sin tratar epoxicamente, 36 vigas monolíticas como testigos, con el fin de correlacionar la resistencia a flexión de las vigas mencionadas anteriormente y 36 cilindros como testigos, con el fin de obtener la resistencia a compresión del diseño de mezcla. A causa de caso fortuito por pandemia, no se fallaron las 12 vigas de 28 días con junta de 8 horas y los 4 cilindros de la misma edad. En las pruebas de la resistencia a la flexión se halla que, para tiempos de formación de 4 horas en edades de 7, 14 y 28 días, la incidencia de la resina epóxica si es significativa para las vigas con presencia de junta fría inclinadas (45°) aumentando en 20%, 6% y 2% respectivamente (los porcentajes son el promedio de 2 datos)es_CO
dc.description.abstractCommonly the elements that are composed of concrete must be interrupted by various compound incidents at the time of the casting process, causing a discontinuity in the element and appearing a joint crack better known as a cold joint, affecting its resistance, by this, it is necessary to create a bonding bridge between the two types of concrete that make up the element to avoid presenting a greater risk of failure. For this reason, this research will evaluate and correlate the flexural strength in simple concrete beams with a (F\'c) of 3000 Psi or 21 MPa partially supported at different ages 7, 14 and 28 days with the presence of vertical cold joints (90°) and inclined (45°), whose formation time was 4, 6 and 8 hours, using the SIKADUR® 32 Primer adhesive as the bonding bridge. 108 specimens distributed as follows, 72 beams with vertical cold joints (90°) and inclined (45°) treated and untreated epoxy, 36 monolithic beams as controls, were produced in order to correlate the flexural resistance of the Previously beams and 36 cylinders as core, in order to obtain the compressive strength of the mix design. Because of a fortuitous case for pandemic, the 12 28-day beams with 8-hour joint and 4 cylinders of the same age were not failed. In the bending resistance tests it is found that, for training times of 4 hours at ages 7, 14 and 28 days, the incidence of epoxy resin if significant for beams with the presence of cold joint inclined (45°) increasing by 20%, 6% and 2% respectively (the percentages are the average of 2 data)en
dc.formatapplication/pdfes_CO
dc.language.isospaes_CO
dc.publisherUniversidad Pontificia Bolivarianaes_CO
dc.rightsAttribution-NonCommercial-NoDerivatives 4.0 International*
dc.rights.urihttp://creativecommons.org/licenses/by-nc-nd/4.0/*
dc.subjectVigas de hormigónes_CO
dc.subjectJuntas fríases_CO
dc.subjectFlexibilidades_CO
dc.subjectCompresibilidades_CO
dc.subjectResistencia de materialeses_CO
dc.titleEvaluación de la resistencia a la flexión en vigas de concreto simple con presencia de juntas frías verticales e inclinadas tratadas epoxicamentees_CO
dc.typeTrabajo de gradoes_CO
dc.creator.degreeIngeniería Civiles_CO
dc.publisher.departmentEscuela de Ingenieríases_CO
dc.publisher.programIngeniería Civiles_CO
dc.type.hasVersionpublishedVersiones_CO
dc.description.sectionalBucaramangaes_CO


Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record

Attribution-NonCommercial-NoDerivatives 4.0 International
Except where otherwise noted, this item's license is described as Attribution-NonCommercial-NoDerivatives 4.0 International